High-temperature electromagnetic wires technical requirements
| Item | Name | Specific | Remark |
| 1 | Electromagnetic wire size B×A | 9.6mm×2.4mm | -- |
| 2 | Electromagnetic wire appearance | The surface is flat, without protrusions, burrs, or damage | After bending |
| 3 | Dimensional tolerance of electromagnetic wires | ±0.05mm | -- |
| 4 | Single length of electromagnetic wire | ≥100m | More longer More better |
| 5 | Dielectric strength of insulation layer | ≥0.15 kV | 400ºC |
| 6 | Insulation layer insulation resistance | ≥5.0MΩ(100Vdc,30s) | 400ºC |
| 7 | Wide edge bending diameter | ≤ 40mm | -- |
| 8 | Narrow edge bending diameter | ≤ 100mm | -- |
| 9 | Conductor material | High temperature copper alloy | -- |
| 10 | Conductor size b×a | 8mm×1.6 mm | -- |
| 11 | Width to thickness ratio of conductors b/a | 5 | -- |
| 12 | Conductor fillet radius---r | 0.50mm+0.05mm | -- |
| 13 | Coating cladding material for conductors | Nickel, iron nickel or other high-temperature and radiation resistant coatings | -- |
| 14 | Thickness of conductor coating | Each side side:15μm to 20μm | -- |
| heat-resistant wire | POT-400AS 1, 6x8 | POZH-700 1, 6x8 |
| maximum permissible operating temperature (24 hours) |
615 degrees | 700 degrees |
| conductive core | copper core with iron -nickel coating | BrXNb alloy BRKHNB alloy |
| insulation | heat-resistant, silicate composition using glass filaments | heat-resistant composition using glass filaments |
| varnish | organosilicon | organosilicon |
| breakdown voltage (600+15 degrees Celsius for 24 hours) |
600V | 550V |
| parameter retention at: | ||
| 260 degrees Celsius | 250000 hours | 240000 hours |
| 350 degrees Celsius | 26000 hours | 25000 hours |
| 400 degrees Celsius | 12000 hours | 14000 hours |
| 600 degrees Celsius | 170 hours | 200 hours |
| warranty storage | period 1 year | 1 year |
| resistance to U-radiation with a dose | of 1660 Mrad | 1780 Mrad |
| relative elongation, not less | than 35% | 30% |